Semiconductor device and method for manufacturing the same

ABSTRACT

A trench is formed by a process which removes a damage layer formed on a sidewall of a low dielectric constant layer, a process which forms a second protection insulating layer by a chemical vapor deposition (CVD) technique and forms a second concave portion by covering a sidewall of the low dielectric constant layer with the second protection insulating layer, and a process which shapes the second protection insulating layer by etch back so that a trench has a sidewall that the second protection insulating layer is selectively formed on a surface of the low dielectric constant layer.

This application is based on Japanese patent application NO. 2008-278351, the content of which is incorporated hereinto by reference.

BACKGROUND

1. Technical Field

The present invention relates to a semiconductor device and a method for manufacturing the same.

2. Related Art

Recently, a copper (Cu) interconnect having low resistance is usually being employed in an advanced semiconductor device pursuing down-scaling and high-speed operation. A copper interconnect is formed by a damascene process. In the damascene process, an interconnect is formed such that a concave portion is formed in an insulating interlayer, a barrier metal layer and a copper layer are formed in the concave portion to embed the concave portion, and portions of the copper layer and the barrier metal layer which are exposed outside the concave portion are removed by a chemical mechanical polishing (CMP) technique. A multi-layer interconnect structure is formed by repetitively performing this procedure.

Also, as a semiconductor device pursues a high performance, a low dielectric constant layer (so-called low-k layer) which is lower in relative dielectric constant (k value) than SiO₂ is used as an insulating interlayer of a multi-layer interconnect structure. There are various kinds of low dielectric constant layers, but low dielectric constant layers are commonly poor in adhesion or mechanical strength. Therefore, there is a problem in that when a trench is formed in a low dielectric constant layer, an altered (degraded) layer is formed on a sidewall of the trench (concave portion) during an etching process or a resist ashing process, and thus an effective k value is increased, causing capacitance between interconnects to be increased.

Japanese Laid-open patent publication No. 2004-72080 discloses a method in which a concave portion is formed in a low dielectric constant layer using a photoresist layer, the photoresist layer is removed, the concave portion is embedded with a conductive layer, and then an altered (degraded) layer is removed. In this method, a dielectric constant layer is embedded on the whole surface of a void generated when the altered layer is removed and is then polished by a CMP process.

Japanese Laid-open patent publication No. 2007-5679 discloses a technology that a via hole is formed in a low dielectric constant layer using a resist layer (by photolithography process), the resist layer is removed, and a damage layer which is formed on a via hole sidewall through resist-removing process is finally removed. Thereafter, the whole surface of the via hole is embedded with a low dielectric constant organic material (such as polybenzoxazole and polyimide which does not have a Si—O bond and has high etching selectivity of equal to or more than 30 to the low dielectric constant layer), and a resist layer is formed thereon to form a trench. The resist layer and the low dielectric constant organic material in the via hole are removed when the trench is formed.

WO 2004/107434 discloses a structure that an insulating barrier layer containing an organic material is formed between an insulating interlayer and a metal interconnect.

SUMMARY

In Japanese Laid-open patent publication No. 2004-72080, however, the altered layer is removed after the concave portion is embedded with the conductive layer to form the copper interconnect. At this time, since the altered (degraded) layer formed along the copper interconnect is removed, the copper interconnect may be peeled. This may causes an open circuit of an interconnect or a short circuit between interconnects.

Also, in Japanese Laid-open patent publication No. 2007-5679, after the damage layer of the via hole is removed, the trench is formed in the low dielectric constant organic material embedded on the whole surface of the via hole. That is, an insulating interlayer in which the interconnect is to be formed is made of a low dielectric constant organic material with high etching selectivity to the lower low electric constant layer. Therefore, there is a problem in that the few alternative materials are available. Also, if the damage layer is formed on a sidewall of the trench during the trench formation, a problem that an effective k value is increased cannot be resolved.

In one embodiment, there is provided a method for manufacturing a semiconductor device, including: forming a trench in a low dielectric constant layer containing carbon formed on a substrate and a first protection insulating layer formed on the low dielectric constant layer. The forming the trench includes: forming a resist layer having an opening pattern for forming a trench on the first protection insulating layer, and forming a first concave portion in the first protection insulating layer and the low dielectric constant layer using the resist layer as a mask; removing a damage layer which is formed on a sidewall of the first concave portion of the low dielectric constant layer when the first concave portion is formed; forming a second protection insulating layer over the whole surface of the substrate by a chemical vapor deposition technique to form a second concave portion in the first protection insulating layer and the low dielectric constant layer by covering the sidewall of the first concave portion in the first protection insulating layer and the low dielectric constant layer with the second protection insulating layer; and shaping the second protection insulating layer by etch back so that the trench has a sidewall where the second protection insulating layer is selectively formed on a surface of the low dielectric constant layer.

In another embodiment, there is provided a semiconductor device, including: a substrate; a low dielectric constant layer formed on the substrate and containing carbon; a first protection insulating layer formed on the low dielectric constant layer; a trench formed in the first protection insulating layer and the low dielectric constant layer; and an interconnect embedded in the trench, wherein the sidewall of the trench has a structure that the surface of the first protection insulating layer protrudes from the surface of the low dielectric constant layer, a second protection insulating layer formed by a chemical vapor deposition technique is embedded at the surface of the low dielectric constant layer in an area below the first protection insulating layer, and the sidewall of the trench is constituted by the second protection insulating layer and the first protection insulating layer.

According to the structure, if the low dielectric constant layer is used as the insulating interlayer in which the trench is formed, even though the damage layer is formed in the low dielectric constant layer, the damage layer is removed, and the second protection insulating layer is formed on a sidewall of the low dielectric constant layer where the damage layer is removed. Therefore, an increment in capacitance between interconnects can be suppressed. Since the trench is formed by shaping the second protection insulating layer after forming the second protection insulating layer, the groove size of the trench can be easily controlled to form the trench.

Also, a suitable combination of the components, and conversion of the expression of the present invention in a method and a device are also effective as an aspect of the present invention.

According to the present invention, it is possible to suppress an increment in capacitance between interconnects by the damage layer formed when the trench is formed in a low dielectric constant layer as the insulating interlayer.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other objects, advantages and features of the present invention will be more apparent from the following description of certain preferred embodiments taken in conjunction with the accompanying drawings, in which:

FIGS. 1A to 1C are cross-sectional views illustrating a procedure for manufacturing a semiconductor device according to an embodiment of the present invention;

FIGS. 2A and 2B are cross-sectional views illustrating a procedure for manufacturing a semiconductor device according to the embodiment of the present invention;

FIGS. 3A to 3D are cross-sectional views illustrating a procedure for manufacturing a semiconductor device according to the embodiment of the present invention;

FIG. 4 is a cross-sectional view illustrating a procedure for manufacturing a semiconductor device according to the embodiment of the present invention;

FIGS. 5A to 5D are cross-sectional views illustrating another example of a procedure for manufacturing a semiconductor device according to the embodiment of the present invention;

FIGS. 6A to 6C are cross-sectional view illustrating a procedure for manufacturing a semiconductor device according to the embodiment of the present invention;

FIGS. 7A to 7C are cross-sectional views illustrating a procedure for manufacturing a semiconductor device according to the embodiment of the present invention;

FIGS. 8A to 8C are cross-sectional views illustrating a procedure for manufacturing a semiconductor device according to the embodiment of the present invention; and

FIG. 9 is a cross-sectional view illustrating a procedure for manufacturing a semiconductor device according to the exemplary of the present invention.

DETAILED DESCRIPTION

The invention will be now described herein with reference to illustrative embodiments. Those skilled in the art will recognize that many alternative embodiments can be accomplished using the teachings of the present invention and that the invention is not limited to the embodiments illustrated for explanatory purposed.

Hereinafter, exemplary embodiments of the present invention will be described with reference to attached drawings. In drawings, like reference numerals denote like parts, and duplicated description will not be repeated.

FIRST EXEMPLARY EMBODIMENT

FIGS. 1A to 4 are cross-sectional views illustrating a procedure of manufacturing a semiconductor device according to the exemplary embodiment of the present invention.

In the exemplary embodiment of the present invention, a procedure for forming a dual damascene trench (including both a wiring trench and a via trench) in a low dielectric constant layer by “via first method” will be described.

A semiconductor device 100 has a structure that an insulating interlayer 110 is formed on a substrate (not shown) which is a semiconductor substrate such as a silicon substrate, and a lower copper interconnect 106 is formed in the insulating interlayer 110. In such a semiconductor device 100, an etching stopper 112, a low dielectric constant layer 114, and a first protection insulating layer 116 are formed on the insulating interlayer 110 and the lower copper interconnect 106 in the described order (FIG. 1A).

The low dielectric constant layer 114 may be made of a material containing carbon. For example, the low dielectric constant layer 114 may be made of a material which contains silicon (Si), oxygen (O) and carbon (C). For example, the low dielectric constant layer 114 may be formed of a SiOC layer, a SiOCH layer, or a porous layer thereof. In the exemplary embodiment of the present invention, the low dielectric constant layer 114 may be configured to have a k value of equal to or less than 3.0. The low dielectric constant layer 114 may be formed by a chemical vapor deposition (CVD) technique or a coating technique.

The insulating interlayer 110 may be formed of a low dielectric constant layer which is made of the same material as the low dielectric constant layer 114. For example, the etching stopper 112 may be formed of a SiCN layer. The first protection insulating layer 116 may be made of a material which functions as a moisture absorption protection layer which prevents moisture from being absorbed into the low dielectric constant layer 114. The first protection insulating layer 116 may be also made of a material which functions to protect the low dielectric constant layer 114 when a CMP process is performed after a conductive layer is embedded in a trench later. For example, the first protection insulating layer 116 may be formed of a SiO₂ layer. The first protection insulating layer 116 may be formed by a CVD technique.

Subsequently, an antireflection layer 118 and a resist layer 120 having an opening pattern 120 for forming a via hole are formed on the first protection insulating layer 116 (FIG. 1B). The opening pattern 120 a for forming a via hole is formed at a location which overlaps the lower copper interconnect 106 when it is seen from a top. The resist layer 120 may be formed using a photolithography technique.

Then, the antireflection layer 118 and the first protection insulating layer 116 are etched using the resist layer 120 as a mask to form an opening pattern 116 a in the first protection insulating layer 116. Subsequently, the low dielectric constant layer 114 is etched using the first protection insulating layer 116 as a mask to form a via hole 136 a in the low dielectric constant layer 114. The via hole 136 a may be formed by a dry-etching technique. As etching gas for etching the low dielectric constant layer 114, fluorocarbon gas such as CF₄ or C₄F₈ may be used, and gas such as N₂ gas, O₂ gas or Ar gas may be added. Thereafter, the resist layer 120 and the antireflection layer 118 are removed by ashing (FIG. 1C). Ashing for removing the resist layer 120 or the like may be performed using gas such as O₂ gas, CO₂ gas, N₂/H₂ gas, NH₃ gas, or He/H₂ gas.

After forming the via hole 136 a, an organic layer 122 is formed over the whole surface of the substrate to fill the via hole 136 a and the opening pattern 116 a. An inorganic layer 124, an antireflection layer 126, and a resist layer 128 having an opening pattern 128 a for forming a trench are formed on the organic layer 122 (FIG. 2A). Here, the opening pattern 128 a for forming a trench is formed at a location which overlaps the via hole 136 a when it is seen from a top. The resist layer 128 may be formed using a photolithography technique.

Subsequently, the antireflection layer 126, the inorganic layer 124, the organic layer 122, and the first protection insulating layer 116 are etched using the resist layer 128 as a mask to form an opening pattern 116 b in the first protection insulating layer 116. The low dielectric constant layer 114 is etched using the first protection insulating layer 116 (and the above layers such as the organic layer 122) as a mask to form a first concave portion 136 b in the first protection insulating layer 116 and the low dielectric constant layer 114 (FIG. 2B). As etching gas for etching the low dielectric constant layer 114, fluorocarbon gas such as CF₄ or C₄F₈ may be used, and gas such as N₂ gas, O₂ gas or Ar gas may be added.

Then, the organic layer 122 is removed by ashing. Here, the resist layer 128, the antireflection layer 126, and the inorganic layer 124 have been already removed in a process for etching other layers, but if such layers remain, they may be removed by the ashing as well. Ashing for removing, for example, the organic layer 122 or the like may be performed using gas such as O₂ gas, CO₂ gas, N₂/H₂ gas, NH₃ gas, or He/H₂ gas.

When a low dielectric constant layer containing carbon is used as the low dielectric constant layer 114, carbon (C) or hydrogen (H) is extracted from the sidewall of the first concave portion 136 b due to influence of the above gas when, for example, the resist layer 128 is removed. Therefore, the sidewall of the low dielectric constant layer 114 is altered to an altered layer (damage layer 130) having a high dielectric constant which is composed of silicon (Si) and oxygen (O) (FIG. 3A). If the damage layer 130 remains existed, capacitance between interconnects of the semiconductor device 100 is increased, and thus there is a problem in that high speed performance of the device gets damaged. Also, if the damage layer 130 remains existed, since moisture is absorbed into the damage layer 130, an effective k value of the damage layer 130 is more increased, and thus capacitance between interconnects is more increased.

For this reason, in the exemplary embodiment of the present invention, the damage layer 130 is removed using, for example, hydrogen fluoride or the like (FIG. 3B). As a result, a recess portion 132 is formed in the low dielectric constant layer 114. That is, the sidewall of the first concave portion 136 b has a structure that the surface of the first protection insulating layer 116 protrudes from the surface of the low dielectric constant layer 114.

Subsequently, a second protection insulating layer 134 is formed over the whole surface of the substrate using a CVD technique such that the sidewall of the first concave portion 136 b of the low dielectric constant layer 114 is covered with the second protection insulating layer 134 to form a second concave portion 136 c in the first protection insulating layer 116 and the low dielectric constant layer 114 (FIG. 3C). As a result, the recess portion 132 formed by removing the damage layer 130 is embedded with the second protection insulating layer 134. In the exemplary embodiment of the present invention, the second protection insulating layer 134 may be configured to have a relative dielectric constant which is equal to or less than that of the low dielectric constant layer 114. For example, the second protection insulating layer 134 may be made of the same material as the low/dielectric constant layer 114. Therefore, since influence of the damage layer 130 disappears, an increment in capacitance between interconnects can be suppressed.

Subsequently, the second protection insulating layer 134 is shaped by etch back to form a trench 136 d that a sidewall is protected by the second protection insulating layer 134 in the low dielectric constant layer 114. At this time, since anisotropic etching is performed, a portion of the second protection insulating layer 134 formed at a top side of a stacking direction of the semiconductor device 100 is selectively removed. Also, since the first protection insulating layer 116 protrudes compared to the low dielectric constant layer 114, a portion of the second protection insulating layer 134 formed on the sidewall of the first protection insulating layer 116 is removed, but a portion of the second protection insulating layer 134 formed on the sidewall of the low dielectric constant layer 114 is protected by the first protection insulating layer 116 and remains without being etched out. Accordingly, the second protection insulating layer 134 can have a structure which is selectively formed only on the sidewall of the low dielectric constant layer 114.

Subsequently, a portion of the etching stopper 112 corresponding to a bottom of the via hole 136 a (and the second protection insulating layer 134 if the second protection insulating layer 134 remains on the bottom of the via hole 136 a) is removed by anisotropic dry etching using, for example, CF₄ gas or a sputtering technique using, for example, an Ar ion, thereby exposing a portion of the lower copper interconnect 106 at the bottom of the via hole 136 a (FIG. 3D). Accordingly, a dual damascene trench which includes the via hole 136 a and the trench 136 d is formed.

In the exemplary embodiment of the present invention, even in the trench 136 d, an opening pattern of the first protection insulating layer 116 maintains the same shape as the opening pattern 128 a for forming the trench of the resist layer 128. When the second protection insulating layer 134 is etched-back, the first protection insulating layer 116 functions as a mask, and a portion of the second protection insulating layer 134 below the first protection insulating layer 116 remains as it is. Therefore, the width of the trench 136 d has the same width of the opening pattern of the first protection insulating layer 116, that is, it has the same width of the opening pattern 128 a for forming the trench of the resist layer 128. Accordingly, a dimension of the groove size can be secured.

Subsequently, a barrier metal layer 140 and a copper layer 142 are formed to embed the via hole 136 a and the trench 136 d, and portions of the barrier metal layer 140 and the copper layer 142 which are exposed outside the trench 136 d are removed by a CMP technique, whereby a copper interconnect 138 is formed (FIG. 4). The copper interconnect 138 is electrically connected to the lower copper interconnect 106.

By the above procedures, manufactured is the semiconductor device 100 that the sidewall of the trench 136 d has a structure that the surface of the first protection insulating layer 116 protrudes from the surface of the low dielectric constant layer 114, the second protection insulating layer 134 formed by a CVD technique is formed on the sidewall of the low dielectric constant layer 114 below the protruding portion of the first protection insulating layer 116, and the sidewall of the trench 136 d is constituted by the second protection insulating layer 134 and the first protection insulating layer 116. Here, the sidewall of the trench 136 d can have a structure that the surface of the second protection insulating layer 134 is matched with the surface of the first protection insulating layer 116.

FIGS. 5A to 5D are cross-sectional views illustrating another example of a procedure for manufacturing a semiconductor device 100 according to the exemplary embodiment of the present invention. Here, the procedure of FIGS. 5A to 5D is different from the above-described procedure in the fact that the etching stopper 112 is removed before forming the second protection insulating layer 134.

In this procedure, after forming the first concave portion 136 b in the first protection insulating layer 116 and the low dielectric constant layer 114 which are described in FIG. 2B, the resist layer 128 and a portion of the etching stopper 112 formed at the bottom of the first concave portion 136 b are removed together. For example, the etching stopper 112 may be removed by anisotropic dry etching using CF₄ gas or a sputtering technique using, for example, an Ar ion (FIG. 5A).

Then, the damage layer 130 is removed using, for example, hydrogen fluoride or the like (FIG. 5B). As a result, a recess portion 132 is formed in the low dielectric constant layer 114. Subsequently, a second protection insulating layer 134 is formed as described in FIG. 3C (FIG. 5C).

Subsequently, the second protection insulating layer 134 is shaped by etch back to form a trench 136 d that a sidewall is protected by the second protection insulating layer 134 in the low dielectric constant layer 114. At this time, due to etch back, a portion of the second protection insulating layer 134 corresponding to a bottom of the via hole 136 a is also removed, and a portion of the lower copper interconnect 106 corresponding to a bottom of the trench 136 d is exposed (FIG. 5D). If the portion of the second protection insulating layer 134 formed at the bottom of the via hole 136 a remains even after etch back, the portion of the second protection insulating layer 134 formed at the bottom of the via hole 136 a may be removed by anisotropic dry etching using, for example, CF₄ gas or a sputtering etch technique using, for example, an Ar ion. Thereafter, as described in FIG. 4, a copper interconnect 138 is formed in the trench 136 d and the via hole 136 a.

In the method for manufacturing the semiconductor device according to the exemplary embodiment of the present invention, the damage layer 130 having a higher (than the low-k material) dielectric constant which is formed on the trench sidewall of the low dielectric constant layer 114 when the trench is formed is removed using hydrogen fluoride or the like, and the sidewall portion recessed by removing the damage layer 130 is recovered by the second protection insulating layer 134. Therefore, it is possible to easily control the size of the trench 136 d while removing the damage layer 130 which causes capacitance between interconnects to be increased. As a result, since an increment in capacitance between interconnects of the semiconductor device 100 can be suppressed and a dimension of the groove size can be secured, a high speed performance can be maintained.

SECOND EXEMPLARY EMBODIMENT

FIGS. 6A to 9 are cross-sectional views illustrating a procedure of manufacturing a semiconductor device according to the exemplary embodiment of the present invention. The exemplary embodiment of the present invention is different from the first exemplary embodiment of the present invention in the fact that a dual damascene trench is formed in a low dielectric constant layer by “trench first method”.

A semiconductor device 100 has a structure that an insulating interlayer 110 is formed on a substrate (not shown) which is a semiconductor substrate such as a silicon substrate, and a lower copper interconnect 106 is formed in the insulating interlayer 110. In such a semiconductor device 100, an etching stopper 112, a first low dielectric constant layer 114 a, an etching stopper 115, a second low dielectric constant layer 114 b, and a first protection insulating layer 116 are formed on the insulating interlayer 110 and the lower copper interconnect 106 in the described order.

The first low dielectric constant layer 114 a and the second low dielectric constant layer 114 b may be made of the same material as the low dielectric constant layer 114 which is described in the first exemplary embodiment of the present invention. The first low dielectric constant layer 114 a and the second low dielectric constant layer 114 b may be made of either the same material or a different material. For example, the first low dielectric constant layer 114 a may be made of a material that is lower in dielectric constant than a silicon oxide layer and has a k value of equal to or less than 3.5.

Subsequently, an antireflection layer (not shown) and a resist layer 150 having an opening pattern 150 a for forming a trench are formed on the first protection insulating layer 116 (FIG. 6A). Here, the opening pattern 150 a for forming a trench is formed at a location which overlaps the lower copper interconnect 106 when it is seen from a top. The resist layer 150 may be formed using a photolithography technique.

Subsequently, the antireflection layer and the first protection insulating layer 116 are etched using the resist layer 150 as a mask to form an opening pattern 116 b in the first protection insulating layer 116. The second low dielectric constant layer 114 b is etched using the first protection insulating layer 116 (and the above layers such as the resist layer 150 or the antireflection layer) as a mask to form a first concave portion 136 b in the first protection insulating layer 116 and the second low dielectric constant layer 114 b (FIG. 6B). As etching gas for etching the second low dielectric constant layer 114 b, fluorocarbon gas such as CF₄ or C₄F₈ may be used, and gas such as N₂ gas, O₂ gas or Ar gas may be added. Thereafter, the resist layer 150 and the antireflection layer are removed by ashing. Ashing for removing, for example, the resist layer 150 and the like may be performed using gas such as O₂ gas, CO₂ gas, N₂/H₂ gas, NH₃ gas, or He/H₂ gas.

At this time, a damage layer 130 is formed on the sidewall of the second low dielectric constant layer 114 b (FIG. 6C). If the damage layer 130 remains existed, since moisture is absorbed into the damage layer 130, an effective k value of the damage layer 130 is increased, and thus there is a problem in that capacitance between interconnects is increased.

For this reason, in the exemplary embodiment of the present invention, the damage layer 130 is removed using, for example, hydrogen fluoride or the like (FIG. 7A). As a result, a recess portion 132 is formed in the second low dielectric constant layer 114 b. That is, the sidewall of the first concave portion 136 b has a structure that the surface of the first protection insulating layer 116 protrudes from the surface of the second low dielectric constant layer 114 b.

Subsequently, a second protection insulating layer 134 is formed over the whole surface of the substrate using a CVD technique such that the sidewall of the first concave portion 136 b of the second low dielectric constant layer 114 b is covered with the second protection insulating layer 134 to form a second concave portion 136 c in the second low dielectric constant layer 114 b (FIG. 7B). As a result, the recess portion 132 formed by removing the damage layer 130 is embedded with the second protection insulating layer 134.

In the exemplary embodiment of the present invention, a kind of a material of the second protection insulating layer 134 is different from that in the first exemplary embodiment of the present invention. In the exemplary embodiment of the present invention, the second protection insulating layer 134 may be made of a material which has resistance (plasma resistance) against gas such as O₂ gas, CO₂ gas, N₂/H₂ gas, NH₃ gas, and He/H₂ gas used to remove the resist layer which will be used to form the via hole later by ashing. For example, the second protection insulating layer 134 may be formed of a SiO₂ layer, a SiOF layer, or a SiOH layer.

Thereafter, a resist layer 152 is formed over the whole surface of the substrate to embed the second concave portion 136 c. Then, an opening 152 a for forming a via hole is formed in the resist layer 152 by a photolithography technique (FIG. 7C). Here, the opening 152 a for forming a via hole is formed at a location which overlaps the lower copper interconnect 106 when it is seen from a top.

Subsequently, the second protection insulating layer 134, the etching stopper 115 and the first low dielectric constant 114 a are etched using the resist layer 152 as a mask to form a via hole 136 a in the first low dielectric constant layer 114 a (FIG. 8A). As etching gas for etching the first low dielectric constant layer 114 a, fluorocarbon gas such as CF₄ or C₄F₈ may be used, and gas such as N₂ gas, O₂ gas or Ar gas may be added.

Subsequently, the resist layer 152 is removed by ashing (FIG. 8B). Ashing for removing the resist layer 152 may be performed using gas such as O₂ gas, CO₂ gas, N₂/H₂ gas, NH₃ gas, or He/H₂ gas. At this time, the sidewall of the second concave portion 136 c is exposed. However, in the exemplary embodiment of the present invention, the second protection insulating layer 134 is made of a material which has resistance (plasma resistance) against gas used to remove the resist layer 152 by ashing. Since the second low dielectric constant layer 114 b is protected by the second protection insulating layer 134, forming of the damage layer can be prevented.

Subsequently, the second protection insulating layer 134 is shaped by etch back to form a trench 136 d that a sidewall is protected by the second protection insulating layer 134 in the second low dielectric constant layer 114 b. At this time, since anisotropic etching is performed, a portion of the second protection insulating layer 134 formed at a top side of a stacking direction of the semiconductor device 100 is selectively removed. Also, since the first protection insulating layer 116 protrudes compared to the second low dielectric constant layer 114 b, a portion of the second protection insulating layer 134 formed on the sidewall of the first protection insulating layer 116 is removed, but a portion of the second protection insulating layer 134 formed on the sidewall of the second low dielectric constant layer 114 b is protected by the first protection insulating layer 116 and remains without being etched out. Accordingly, the second protection insulating layer 134 can have a structure which is selectively formed only on the sidewall of the second low dielectric constant layer 114 b.

In the exemplary embodiment of the present invention, even in the trench 136 d, an opening pattern of the first protection insulating layer 116 maintains the same shape as the opening pattern 150 a for forming the trench of the resist layer 150. When the second protection insulating layer 134 is etched-back, the first protection insulating layer 116 functions as a mask, and a portion of the second protection insulating layer 134 below the first protection insulating layer 116 remains as it is. Therefore, the width of the trench 136 d has the same width of the opening pattern of the first protection insulating layer 116, that is, it has the same width of the opening pattern 150 a for forming the trench of the resist layer 150. Accordingly, a dimension of the groove size can be secured.

Then, a portion of the etching stopper 112 corresponding to a bottom of the via hole 136 a (and the second protection insulating layer 134 if the second protection insulating layer 134 remains on the bottom of the via hole 136 a) is removed by anisotropic dry etching using, for example, CF₄ gas or a sputtering technique using, for example, an Ar ion, thereby exposing a portion of the lower copper interconnect 106 at the bottom of the via hole 136 a (FIG. 8C). Accordingly, a dual damascene trench which includes the via hole 136 a and the trench 136 d is formed.

Subsequently, a barrier metal layer 140 and a copper layer 142 are formed to embed the via hole 136 a and the trench 136 d, and portions of the barrier metal layer 140 and the copper layer 142 which are exposed outside the trench 136 d are removed by a CMP technique, whereby a copper interconnect 138 is formed (FIG. 9). The copper interconnect 138 is electrically connected to the lower copper interconnect 106.

By the procedure, manufactured is the semiconductor device 100 that the sidewall of the trench 136 d has a structure that the surface of the first protection insulating layer 116 protrudes from the surface of the second low dielectric constant layer 114 b, the second protection insulating layer 134 formed by a CVD technique is formed on the sidewall of the second low dielectric constant layer 114 b below the protruding portion of the first protection insulating layer 116, and the sidewall of the trench 136 d is constituted by the second protection insulating layer 134 and the first protection insulating layer 116. Here, the sidewall of the trench 136 d can have a structure that the surface of the second protection insulating layer 134 is matched with the surface of the first protection insulating layer 116.

In the method for manufacturing the semiconductor device according to the exemplary embodiment of the present invention, the damage layer 130 having a high dielectric constant which is formed on the trench sidewall of the second low dielectric constant layer 114 b when the trench is formed is removed using hydrogen fluoride or the like, and the sidewall portion recessed by removing the damage layer 130 is recovered by the second protection insulating layer 134. Therefore, it is possible to easily control the size of the trench 136 d to form the trench 136 d while removing the damage layer 130 which causes capacitance between interconnects to be increased. As a result, since an increment in capacitance between interconnects of the semiconductor device 100 can be suppressed and a dimension of the groove size can be secured, a high speed performance can be maintained.

Hereinbefore, the exemplary embodiments of the present invention have been described with reference to the drawings, but these are for illustrative purposes and can employ various configurations other than described above.

In the exemplary embodiments of the present invention, the first exemplary embodiment has a structure that the etching stopper is not formed when the trench is formed in the insulating interlayer like the etching stopper 115 which is described in the second exemplary embodiment. However, the first exemplary embodiment can use a structure that the first low dielectric constant layer 114 a, the etching stopper layer 115 and the second low dielectric constant layer 114 b are stacked, which is described in the second exemplary embodiment, instead of the low dielectric constant layer 114. Also, the second exemplary embodiment can use the low dielectric constant layer 114 described in the first exemplary embodiment instead of a structure that the first low dielectric constant layer 114 a, the etching stopper layer 115 and the second low dielectric constant layer 114 b are stacked.

It is apparent that the present invention is not limited to the above embodiment, and may be modified and changed without departing from the scope and spirit of the invention. 

1. A method for manufacturing a semiconductor device, comprising: forming a trench in a low dielectric constant layer containing carbon formed on a substrate and a first protection insulating layer formed on said low dielectric constant layer, wherein said forming said trench includes: forming a resist layer having an opening pattern for forming a trench on said first protection insulating layer, and forming a first concave portion in said first protection insulating layer and said low dielectric constant layer using said resist layer as a mask; removing a damage layer which is formed on a sidewall of said first concave portion of said low dielectric constant layer when said first concave portion is formed; forming a second protection insulating layer over the whole surface of said substrate by a chemical vapor deposition technique to form a second concave portion in said first protection insulating layer and said low dielectric constant layer by covering the sidewall of said first concave portion in said first protection insulating layer and said low dielectric constant layer with said second protection insulating layer; and shaping said second protection insulating layer by etch back so that said trench has a sidewall where said second protection insulating layer is selectively formed on a surface of said low dielectric constant layer.
 2. The method according to claim 1, wherein said first protection insulating layer and said second protection insulating layer are exposed at the sidewall of said trench.
 3. The method according to claim 1, wherein in said removing said damage layer, the sidewall of said first concave portion has a structure that the surface of said first protection insulating layer protrudes from the surface of said low dielectric constant layer, and in said shaping said second protection insulating layer by etch back, said second protection insulating layer is embedded at the surface of said low dielectric constant layer in an area below said first protection insulating layer.
 4. The method according to claim 1, wherein said forming said first concave portion includes removing said resist layer by ashing after forming said first concave portion.
 5. The method according to claim 1, wherein said low dielectric constant layer is a SiOC layer or a SiOCH layer.
 6. The method according to claim 1, further comprising, before said forming said trench, forming a via hole which is to be consecutively formed with the trench to constitute a dual damascene trench, wherein said second protection insulating layer has a relative dielectric constant which is equal to or less than a relative dielectric constant of said low dielectric constant layer.
 7. The method according to claim 6, wherein said second protection insulating layer is made of the same material as said low dielectric constant layer.
 8. The method according to claim 1, further comprising, after said forming said trench, forming a via hole which is to be consecutively formed with said trench to constitute a dual damascene trench, wherein said second protection insulating layer is a SiO₂ layer, a SiOF layer, or a SiOH layer.
 9. The method according to claim 1, wherein said second protection insulating layer is a SiO₂ layer, a SiOF layer, a SiOH layer, a SiOC layer, or a SiOCH layer.
 10. The method according to claim 1, wherein said low dielectric constant layer is formed on a lower interconnect formed on said substrate, and in said forming said trench, said lower interconnect is exposed when said trench is formed.
 11. The method according to claim 1, wherein said first protection insulating layer is a SiO₂ layer. 